Toe link
The toe link impressively demonstrates the high bending radius and forming which can be achieved with SZBS800 in spite of the high yield strength of more than 680 MPa, in process-safe manner and without edge cracks. Thanks to its high fatigue strength, the SZBS800 is particularly well suited for use in the dynamically highly stressed toe link.
During stamping tests, the StronSal® zinc magnesium coating showed significantly lower zinc abrasion in the pressing tools than conventional zinc coatings (hot-dipped and electrolytic galvanizing). This enables resource-saving reductions of the zinc layer thickness compared to conventional galvanizing, as well as a higher number of presses during the forming process.
| Material: | SZBS800+ZM |
| Thickness: | 1.8 mm |
| Surface: | StronSal® coated (ZM70/70) |